Alclad 2014 T3 T4 T6 O Aluminum Plate
2014 aluminum plate is a popular material among the 2000 series aluminum alloys, second only to 2024 aluminum alloy. 2014 aluminum plates have high strength, good cutting performance, and excellent machining performance, and are mostly used in applications that require high strength and hardness (including high temperatures).
The corrosion resistance of 2014 aluminum alloys is poor, so alclad aluminum plates are usually used to improve corrosion resistance. If the bare 2014 aluminum is to be exposed to the natural environment, it should be painted as a corrosion protection measure.
Chalco Alclad 2014 hot selling sizes
Hot selling size: 1525mm x 3660mm, 1250mm x 2550mm
Hot selling thickness: 10mm, 12mm, 15mm, 20mm, 25mm, 30mm, 35mm, 40mm, 45mm, 50mm, 55mm, 60mm, 65mm, 70mm, 75mm, 80mm, 85mm, 90mm, 100mm, 110mm, 120mm, 150mm, 160mm, 180mm, 200mm, 250mm
Mechanical properties of Alclad 2014 aluminum plate
| Temper | Thickness mm | Tensile strength Rm | Yield strength Rp0.2 | Elongation min.% A50mm | |
|---|---|---|---|---|---|
| Min | Max | MPa | MPa | ||
| O | 0.50 | 0.63 | ≤205 | ≤95 | 16 |
| O | 0.63 | 1.00 | ≤220 | ≤95 | 16 |
| O | 1.00 | 2.50 | ≤205 | ≤95 | 16 |
| O | 2.50 | 12.50 | ≤205 | ≤95 | 16 |
| O | 12.50 | 25.00 | ≤220 | - | - |
| T3 | 0.50 | 0.63 | 370 | 230 | 14 |
| T3 | 0.63 | 1.00 | 380 | 235 | 14 |
| T3 | 1.00 | 2.50 | 395 | 240 | 15 |
| T3 | 2.50 | 6.30 | 395 | 240 | 15 |
| T4 | 0.50 | 0.63 | 370 | 215 | 14 |
| T4 | 0.63 | 1.00 | 380 | 220 | 14 |
| T4 | 1.00 | 2.50 | 395 | 235 | 15 |
| T4 | 2.50 | 6.30 | 395 | 235 | 15 |
| T6 | 0.50 | 0.63 | 425 | 370 | 7 |
| T6 | 0.63 | 1.00 | 435 | 380 | 7 |
| T6 | 1.00 | 2.50 | 440 | 395 | 8 |
| T6 | 2.50 | 6.30 | 440 | 395 | 8 |
Chemical composition of Alclad 2014 aluminum plate
| Element | Composition % |
|---|---|
| Al | 90.4-95 % |
| Cr | ≤0.10 % |
| Cu | 3.9-5.0 % |
| Fe | ≤0.70 % |
| Mg | 0.20-0.80 % |
| Mn | 0.40-1.2 % |
| Si | 0.50-1.2 % |
| Ti | ≤0.15 % |
| Zn | ≤0.25 % |
| Other, each | ≤0.05 % |
| Other, total | ≤0.15 % |
Features of Alclad 2014 aluminum plate
- High hardness, high strength, and can be strengthened through heat treatment to improve hardness;
- Excellent processability;
- Low density, high specific modulus, good thermal conductivity and conductivity;
- Good weldability, facilitating welding manufacturing and maintenance;
- It can be applied in situations that require high strength, hardness, and high temperatures.
Application of Alclad 2014 aluminum plate
- In the aerospace industry to manufacture key components such as aircraft structures, wings, skins, and engine components.
- In the automotive manufacturing field to manufacture key components such as body structures, frames, suspension components, etc.
- In the defense industry to manufacture aircraft components, missile components, and other equipment with high strength and lightweight requirements.
- Applied in high-temperature industries to manufacture high-temperature resistant equipment such as gas turbine components and heat exchangers.
- Manufacture high-performance sports equipment, such as bicycle frames, scooter components, etc.
- In engineering field for building bridges, tower cranes, and other structures, utilizing their high strength to improve the load-bearing capacity of the structure.